90 105 olie slip zachte kabel PVC elastomeer verbinding

FOB Referentie prijs:Krijg recentste prijs
US$ 3,00 - US$ 3,50 / Kilogram | 3000 Kilogram/kg (Min. Order)
Verzending:
Ondersteuning Zeevracht
rapport Verdachte Activiteit
Overzicht:
Snelle gegevens
plaats van herkomst:
Jiangxi, China
naam van het merk:
Longtai
modelnummer:
PVC Hars
Kleur:
Kleurrijke
Type:
Synthetische Hars
Gebruik:
Elektronische Draad
Certificaat:
SGS
Materiaal:
Virgin Pvc Hars
Product naam:
Grade
Toepassing:
Draad Kabel
Standaard:
UL
Leveringsvermogen
Leveringsvermogen:
1000 Ton/Tons per Month
Verpakking en verzending
Verpakkingsdetails
Tassen
Port
shenzhen
Levertijd: :
7----10days

 

Product Description
Test Reference: UL62&UL2556Insulation P/N: Black Jacket
ItemRequirementTest ResultsRemark
JacketSize of Inuslatormm²13.86T:2.31mm                       W: 6.0mm
Before AgeingElongation at Break> 200%410      405     410Velocity of the tester  500±25mm/mikn
Pull ForceKGF12.38   12.49  13.53
Tensile Strength>085KGF/mm²0.89     0.90     0.98
After Ageing               (105 ℃)Elongation at Break> %425      435      435Test Period:                       16:00 Mar.29-   16:00 Apr 05
Pull ForceKGF14.02   12.63  12.73
Tensile Strength>KGF/mm²1.01     0.91    0.92 
The Remain Elongtaion Rate> 75%104       107     107Temperature:136 ℃ Duration:168h
The Remain Tensile Strength Rate> 75%110        99      100
Jacket Oil              Aging TestElongation at Break> %310       320     320  Test Period:                       16:00 Mar.29- 16:00 Apr 05
Pull ForceKGF10.34   10.57    10.77 
Tensile Strength>KGF/mm²0.75      0.76     0.78 
The Remain Elongtaion Rate> 75%76         78        78  Temperature:136 ℃ Duration:168h
The Remain Tensile Strength Rate> 75%82        83         85  
Electrical PerformanceJacket               Resistance Test> 100MΩ246.3 GΩDC: 500V/1min
Physical PerformanceHeat Deformation Test< 50%47.6  45.8  46.7  150℃ X 1h X 2000g
Heat Shock Testwithout crackingwithout cracking150℃ X 1hX Ø34.9mm
Cold Impact Test Cable Without Cracking 
Cold Bend Testwithout crackingwithout cracking‘- 40℃X 4h X Ø31.8mm
Flammability Test (FT-1)a. The delay time at every time is not more than 60s after remove flame;                                       b. The bumed area of indication flag on the testing sample is not more than 25%ok 
Flammability Test (FT-2)1.The length of the charred portion of the specimen of cord shall not exceed 100mm not shall flaming particles ignitecotton.                                                       2. Flameless charring of the cotton shall be ignored< 100mm 
Cable Flexibility TestCoil 10ft of cable into a cyliner with an inner diameter that is between 260 and 275 mm in diameter (a typical US 5 gal bucket has this diameter) in a single layer with no gaps between the coils. The end of the cable on the top winding is secured to the 2nd turn of the coil. Place the cable and cylinder sample inside a chamber that has been preconditioned to minus -30 ℃ with uncontrolled humidity and leave it for a minimun of  2 hours, Remove the sample from th cylinder and support the top turn of cable at the top of the coil 4 feet above the floor or supporting surface, then allow the other end of the cable to descend under its own weight. Measure the time that it takes for the cable to first touch the floor or supporting surface. Pass/ Fail: if the end of the cable reaches the supporting surface within 2 minutes for the 32 A cable, the criteria is met, 16A cable TBDTime is 97 seconds cable reaches the supporting surface 

Specification
2. other pvc compound

 

 GradeUL 80℃ standard cable material UL 105℃ standard cable material 
PropertiesUnits/
Terms
EUL80-K/UL1007EUL80-K/UL1015EUL105-K/UL1015EUL105-K/UL1007
 
Temp Resistance 
8080105105

Hardness
Shore A89±2A89±2A88A±2A (45P)88A±2A (45P)

Tensile Strength
PSI≥2000≥1900≥1700≥1750

Elongation at break
%≥200≥190≥180≥180

Cold bend temp 
℃/4H-20-20-20-20

Insulation Resistance
M•KM≥2.5≥2.5≥2.5≥10

Burning test
--VW-1VW-1VW-1VW-1

Aging temp 
113113136136

Aging time
H168168168168

T.S After Aging
PSI≥2200≥2000≥1900≥1950

T.S residual rate
%≥70≥70≥75≥75

Elongation at break after aging
%≥160≥170≥130≥135

Elongation residual rate
%≥65≥65≥65≥65

Special Gravity
g/cm31.43±0.021.43±0.021.43±0.021.43±0.02

 

 

 

 

1.Technical specifications of 70 pvc compound

 

Technical specifications of  90 pvc compound

 

Tensile strength

MPa

20

Fracture tensile strain

%

330

Ageing temperature

100

Ageing time

h

240

Tensile strength after ageing

MPa

21.5

Max change of tensile strength

%

+8

After ageing fracture tensile strain

%

310

Max change of fracture tensile strain

%

-6

Thermal deformation

%

28

Thermal ageing quality loss

g/m2

9

200 thermal stability time

min

120

20 volume resistivity

 Ω.cm

2.0*1010

 

 

u Mag
Niet precies wat u zoekt? Eén aanvraag, meerdere offertes Nu offertes ontvangen >>
De resultaten van deze producten of leveranciers zijn automatisch voor u vertaald door onze vertaaltool. Als u problemen ondervindt met de vertaalresultaten, zijn uw suggesties van harte welkom.
Alle informatie over producten en leveranciers op deze pagina die wordt weergegeven in een taal anders dan Engels is informatie van www.alibaba.com die automatisch is vertaald door de vertaaltool. Als u een vraag over of suggestie hebt voor de kwaliteit van de automatische vertaling, mailt u ons via english.trans@service.alibaba.com. De vertaling is een volledig automatisch proces dat wordt voltooid door techniek. Alibaba.com heeft niet deelgenomen in de vertaling en kent en beheert de vertaling of de inhoud van vermeldingen niet. Alibaba.com en zijn dochterondernemingen wijzen bij dezen uitdrukkelijk elke garantie, expliciet of impliciet, en verantwoordelijk af voor verlies die voortkomt uit of in vertrouwen op automatisch vertaalde informatie, of die wordt veroorzaakt door een technische fout in de vertaaltool.